Experiments show that:

When the DCP ≥ 0.6: product surface cracking, wrinkled; DCP <0.6: better visual surface of the article; the above results are analyzed: the experimental conditions, when the DCP is greater than or equal to 0.6, the crosslinking rate too large, then the AC had a chance to fully decompose, COLOR FELT MANUFACTURER melt viscosity has been great, the bubble does not fully inflate, so the bubble pressure in vivo large (the force is temporary equilibrium), but the pressure does not destroy COLOR FELT MANUFACTURER crosslinking system, when unload the outside pressure, cracks, wrinkles. From theorized that: when the amount of less than a certain value, DCP, this value corresponds to the amount of a gel, and this gel is to get a good amount of the minimum of foam (about 65%).

Figure 1 shows that: when the amount of color felt manufacturer DCP is between 0.1 and 0.5, the product of the apparent density with the total amount of DCP decreases. This is the experimental conditions, color felt manufacturer DCP is helpful to increase the melt viscosity, thereby effectively preventing the escape of gas in the melt, so that the color felt manufacturer apparent overall density reduction products.

As can be seen from Figure 2: Under the experimental conditions, the tensile strength with DCP content first increases and then decreases, color felt manufacturer and in the DCP = 0.3 Department has the maximum value. In theory, color felt manufacturer the tensile strength should vary with DCP content decreases, but the experiment did not sample preparation crusts removed, so that its impact cannot be ignored, even in the small amount of DCP dominant factors that make tensile strength increased to some extent; when DCP amount exceeds 0.3, the apparent overall density of products is the dominant factor, the tensile strength decreases.